A tabela 1.13 apresenta dados de composição química de alguns aços Cr-Mo pela ASTM.
|
Tipo |
Forjados |
Tubos |
Tubulações |
Fundidos |
Placas |
|
0,5Cr-0,5Mo |
A182-F2 |
--- |
A335-P2, A369-FP2, A426-CP2 |
--- |
A387-Grau 2 |
|
1Cr-0,5Mo |
A182-F12, A336-F12 |
--- |
A335-P12,A369-FP12, A426-CP12 |
--- |
A387-Grau 12 |
|
1,25Cr-0,5Mo |
A182-F11, A336-F11/F11A, A541-C11C |
A199-T11, A200-T11, A213-T11 |
A335-P11, A369-FP11, A426-CP11 |
A217-WC6, A356-Grau 6, A389-C23 |
A387-Grau 11 |
|
2,25Cr-1Mo |
A182-F22/F22a, A336-F22/F22A, A541-C22/22D |
A199-T22, A200-T22, A213-T22 |
A217-WC9, A356-Grau10
|
A387-Grau21 |
|
|
3Cr-1MoV |
A182-F21b |
--- |
--- |
--- |
--- |
|
5Cr-0,5Mo |
A182-F5/F5a, A336-F5/F5A, A473-501/502 |
A199-T5, A200-T5, A213-T5 |
A335-P5, A369-FP5, A426-CP5 |
A 217-C5 |
A387-Grau5 |
|
5Cr-0,5MoSi |
--- |
A213-T5, A213-T5b |
A335-P5B, A426-CP5b |
--- |
--- |
|
5Cr-0,5MoTi |
--- |
A213-T5c |
A335-P5c |
--- |
--- |
|
7Cr-0,5Mo |
A182-F7, A473-501A |
A199-T7, A200-T7, A213-T7
|
A335-P7, A369-FP7, A426-CP7 |
--- |
A387-Grau7 |
|
9Cr-1Mo |
A182-F9, A336-F9, A473-501B
|
A199-T9, A200-T9, A213-T9 |
A335-P9, A369-FP9, A426-CP9 |
A217-C12 |
A387-Grau9 |
Nos aços baixa liga (menos de 10 % de cada elemento) ao Cr e Mo: o cromo, mesmo em baixos teores aumenta a resistência mecânica, a tenacidade e a resistência ao impacto e em teores mais elevados aumenta a resistência ao desgaste, devido á formação de carbonetos de cromo duros; o molibdênio aumenta a resistência mecânica (devido à formação de carbonetos de molibdênio), reduz a susceptibilidade á fragilização por revenido e melhora as propriedades mecânicas em temperaturas elevadas. Esses aços são utilizados em diversas aplicações estruturais.